Soveltuu hyvin käytettäväksi hiilikuidun, lasikuidun, aramid ja muiden kuitujen kanssa.

Työskentelyaika: 40 minuuttia (100g /20C)


Epoxy resin L + Kovetin L (40min) 1kg

Tuotenumero: RG1001101
26,00 €Hinta
  • Epoxy Resin L and Hardener L 

    The resin system Epoxy Resin L + Hardener L yields superior impregnating and wetting properties towards carbon, glass, aramid and natural fibres.

    • Low viscosity
    • Highly transparent
    • High degree of UV stability
    • Tack-free curing even of thin layers
    • Glass transition temperature (Tg) max. 76 °C (post-curing at 60 °C / 15 h)
    • High static and dynamic strength
    • Free of nonylphenol and DETA

    Processing time: 40 minutes (100 g / 20 °C)

    Mixing ratio:
    100 : 40 parts by weight resin : hardener 
    100 : 45 parts by volume resin : hardener

    It exhibits a very good price/performance ratio and is suitable for the following processing procedures: 

    • Hand laminating
    • Vacuum moulding
    • Press moulding

    Expertise for the resin system Epoxy Resin L + Hardener L: this system is not cytotoxic (cell damaging), important for applications in medical purposes.

    Mechanical properties (Neat resin after curing)

    Flexural test 

    Flexural strength (DIN EN ISO 178): 111 MPa
    Flexural modulus (DIN EN ISO 178): 2.960 MPa

    Tensile test 

    Tensile strength (DIN EN ISO 527): 69 MPa
    Elongation at break: 4.7 %

    Compression test

    Compressive strength (DIN EN ISO 1426): 91 MPa

    General information about the system "Epoxy Resin L" with Hardeners S, L, CL, EPH 500, EPH 161, W 300, GL 1 and GL 2

    • Low viscosity, free of solvents and fillers
    • Fast impregnation of glass, aramid, carbon and natural fibres
    • High static and dynamic strength (GL approval with the Hardeners GL 1 and GL 2 being present

    Epoxy Resin L with the corresponding Hardeners S, L, CL, EPH 500, EPH 161, W 300, GL 1 and GL 2 is the most commonly used laminating and adhesive resin in R&G`s delivery programme.

    In conjunction with the Hardeners S (15 minutes), L (40 minutes), CL (60 minutes), EPH 500 (60 minutes), EPH 161 (90 minutes), W 300 (300 minutes), GL 1 (30 minutes) and GL 2(210 minutes), this epoxy resin exhibits similar mechanical properties to those of the laminating systems usual aerospace .Its heat deflection temperature reaches from 60 °C (S, L, EPH 500, W 300), to 80 °C (GL 1 and GL 2, after post-curing), to 95 °C (CL, after post-curing) and finally to 120 °C (EPH 161, after post-curing).

    Its low surface tension, good adhesion, and minimal curing shrinkage makes the Epoxy Resin L ideal for bonding wood, metal, foamed polystyrene like Styropor® etc. It can be processed in all of the customary methods, e.g. hand lay-up, pressure and vacuum impregnation, press moulding and filament winding.